Colorant Sources																					PDH	2/18/12
"Cobalt" Types				Cobalt			Carbon			Oxygen			Hydrogen			Total
				# Atoms	Atomic Mass		# Atoms	Atomic Mass		# Atoms	Atomic Mass		# Atoms	Atomic Mass		Atomic Mass	Cobalt		Relative Strength
Green Cobalt Oxide	CoO			1	58.93					1	16					74.93	79%		1.00	1.11	1.07	1.59	1.41
Back Cobalt Oxide	Co2O3			2	58.93					3	16					165.86	71%		0.90	1.00	0.97	1.43	1.28
Blue Cobalt Oxide	Co3O4			3	58.93					4	16					240.79	73%		0.93	1.03	1.00	1.48	1.32
Cobalt Carbonate	CoCO3			1	58.93		1	12		3	16					118.93	50%		0.63	0.70	0.67	1.00	0.89
Cobalt Basic Carbonate	Co(CO3)Co(OH)2			2	58.93		1	12		5	16		2	1		211.86	56%		0.78	0.76	0.76	1.12	1.00
"Copper" Sources				Copper			Carbon			Oxygen			Hydrogen			Total
				# Atoms	Atomic Mass		# Atoms	Atomic Mass		# Atoms	Atomic Mass		# Atoms	Atomic Mass		Atomic Mass	Copper		Relative Strength
Black Copper Oxide	CuO	Cupic Oxide		1	63.55					1	16					79.55	80%		1.00	0.90	1.55	1.39
Red Copper Oxide	Cu2O	Cuprous Oxide		2	63.55					1	16					143.1	89%		1.11	1.00	1.73	1.55
Copper Carbonate	CuCO3	Cupric Carbonate		1	63.55		1	12		3	16					123.55	51%		0.64	0.58	1.00	0.89
Copper Basic Carbonate	Cu(CO3)Cu(OH)2	Cupric Carbonate Basic		2	63.55		1	12		5	16		2	1		221.1	57%		0.72	0.65	1.12	1.00
"Iron" Sources				Iron						Oxygen						Total
				# Atoms	Atomic Mass					# Atoms	Atomic Mass					Atomic Mass	Iron		Relative Strength
Not stable at room temperature	FeO	Ferrous Oxide		1	55.84					1	16					71.84	78%		1.00	1.11	1.07
Red Iron Oxide	Fe2O3	Ferric Oxide		2	55.84					3	16					159.68	70%		0.90	1.00	0.97
Black Iron Oxide (Magnetite)	Fe3O4	Ferrous-ferric Oxide		3	55.84					4	16					231.52	72%		0.93	1.03	1.00
"Nickel" Sources				Nickel			Carbon			Oxygen						Total
				# Atoms	Atomic Mass		# Atoms	Atomic Mass		# Atoms	Atomic Mass					Atomic Mass	Nickel		Relative Strength
Black Nickel Oxide	Ni2O3			2	58.69					3	16					165.38	71%		1.00	0.90	1.44
Green Nickel Oxide	NiO	Bunsenite, very rare		1	58.69					1	16					74.69	79%		1.11	1.00	1.59
Green Nickel Carbonate	NiCO3			1	58.69		1	12		3	16					118.69	49%		0.70	0.63	1.00